Carbon Fiber Fabric Strengthening System
High-strength unidirectional carbon fiber fabric for externally bonded reinforcement.
Carbon fiber fabric is a unidirectional, high-strength fabric used in the wet lay-up strengthening of reinforced concrete, masonry and timber structures. Applied with a matched epoxy resin system, it bonds to the structural surface to add tensile capacity for flexural, shear and confinement reinforcement.
Each roll is woven from continuous high-strength carbon fiber tow under controlled tension for consistent fiber alignment and areal weight.
| Product | Areal Weight | Nominal Thickness | Tensile Strength | Elastic Modulus |
|---|---|---|---|---|
| FSC200 | 200 g/m² | 0.111 mm | 3,500–4,500 MPa | 230–240 GPa |
| FSC230 | 230 g/m² | 0.128 mm | 3,500–4,500 MPa | 230–240 GPa |
| FSC300 | 300 g/m² | 0.167 mm | 3,500–4,500 MPa | 230–240 GPa |
| FSC600 | 600 g/m² | 0.333 mm | 3,800–4,400 MPa | 230–235 GPa |
Available widths: 10 / 15 / 20 / 25 / 30 / 50 / 60 cm (custom widths on request). Roll length: 100 m (FSC200/230/300), 50 m (FSC600). Supplied with matched epoxy primer, saturating resin and levelling adhesive for a complete system.
Typical applications
- Beam flexural and shear strengthening
- Column confinement and seismic retrofitting
- Slab and floor strengthening
- Repair of damaged or under-designed concrete members